大体积混凝土温度分析与裂缝控制.doc

作者：曹运周 董佳佳 王程锋 赵永峰 【摘??要】大体积混凝土工程由于结构截面大，混凝土浇注后，水泥放出大量水化热，混凝土温度升高，而且混凝土导热不良，相对散热较小。因此，混凝土内部水化热积聚不易散发，外部则散热较快，很容易由于温度的不均衡分布产生应力，故而产生温度裂缝。本文详细地介绍了大体积混凝土产生裂缝的机理，并从材料、设计、施工方面提出控制手段，引用具体实例进行论证。【关键词】大体积混凝土施工；裂缝；温度应力；测温【Abstract】Mass concrete works great because of structural cross-section, concrete pouring, the evolution of considerable heat of hydration of cement, concrete temperature, and the concrete thermal conductivity of non-performing, relatively small heat. Therefore, the concrete hydration heat build-up is not easy dissemination of internal and external is cooling rapidly, it is easy because of the uneven distribution of temperature cause stress and therefore I produce temperature cracks. This article describes in detail cracks in mass concrete mechanism, and from materials, design, construction and put forward controls, citing specific examples to demonstrate.【Key words】Mass concrete construction; Crack; Temperature stress; Temperature? ?? ???1. 前言? ?? ???近几年来，全国各地工程规模日趋扩大，结构形式日益复杂，工业与民用建筑中对大体积混凝土需求越来越多。由于其体积大，表面小，水泥水化热释放比较集中，内部温升比较快，当混凝土内外温差较大时，会使混凝土产生温度裂缝，影响结构安全和正常使用，所以必须从根本上分析它，来保证施工的质量。? ?? ???2. 裂缝成因分析? ?? ???大体积混凝土一般是指实体截面最小尺寸大于或等于1m的混凝土构件。它的表面系数比较小，水泥水化热释放比较集中，内部温升比较快。混凝土内外温差较大时，会使混凝土产生温度裂缝，影响结构安全和正常使用? ?? ???混凝土裂缝分为以下几种类型：弯距剪力等外力荷载引起的裂缝；干燥收缩引起的裂缝；混凝土自身收缩引起的裂缝；温度裂缝。? ?? ???大体积混凝土工程，水泥用量多，结构截面大，因此，混凝土浇注后，水泥放出大量水化热，混凝土温度升高。由于混凝土导热不良，体积过大，相对散热较小。因此，混凝土内部水化热积聚不易散发，外部则散热较快，依据热胀冷缩的原理，结构自身约束由伴随温度变化引起的建筑物体积变化产生应力，一但拉伸应力＞抗拉强度则混凝土产生裂缝。? ?? ???故控制大体积混凝土开裂必须从两方面入手。一方面，提高混凝土的抗拉强度，使其足够大，大到各种因素引起的开裂应小于它，另一方面，控制温度应力，使其尽可能小，永远小于混凝土的抗拉强度。? ?? ???3. 裂缝控制手段? ?? ???要避免混凝土裂缝的产生需从材料、设计、施工上来进行控制。? ?? ???3.1??材料控制? ?? ???(1)水泥：使用水化热较低的水泥以及尽量降低单位水泥用量；水泥在水化过程中要释放出一定的热量，而大体积混凝土结构断面较厚，表面系数相对较小，所以水泥发生的热量聚集在结构内部不易散失。这样混凝土内部的水化热无法及时散发出去，以至于越积越高，使内外温差增大。单位时间混凝土释放的水泥水化热，与混凝土单位体积中水泥用量和水泥品种有关，并随混凝土的龄期而增长。由于混凝土结构表面可以自然散热，普通混凝土内部的最高温度，多数发生在浇筑后的最初3~7天。? ?? ???(2)掺合料和外加剂：在混凝土中掺入水泥用量0.25%的减水剂，可同时减少10%的水泥用量，从而降低水化热的产生；在混凝土中掺入粉煤灰，不仅可代替水泥用量，而且可大大改善混凝土的可泵性和工作性，从而