一、 拉伸实验···············································································2 二、 压缩实验···············································································4 三、 拉压弹性模量E测定实验···················································6 四、 低碳钢剪切弹性模量G测定实验·······································8 五、扭转破坏实验····································································10 六、 纯弯曲梁正应力实验··························································12 七、 弯扭组合变形时的主应力测定实验··································15 八、 压杆稳定实验······································································18
一、拉伸实验报告标准答案
实验目的: 见教材。 实验仪器 见教材。
实验结果及数据处理: 例:(一)低碳钢试件
强度指标:
Ps=__22.1___KN屈服应力 ζs= Ps/A __273.8___MPa P b =__33.2___KN强度极限 ζb= Pb /A __411.3___MPa 塑性指标:
伸长率??
L1-LL
?100%?
A?A1
A
33.24 %面积收缩率??
?100%?
68.40 %
低碳钢拉伸图:
(二)铸铁试件
强度指标:
最大载荷Pb =__14.4___ KN
强度极限ζb= Pb / A = _177.7__ M Pa
问题讨论:
1、 为何在拉伸试验中必须采用标准试件或比例试件,材料相同而长短不同的试件延伸率是否相同?
答:拉伸实验中延伸率的大小与材料有关,同时与试件的标距长度有关.试件局部变形较大的断口部分,在不同长度的标距中所占比例也不同.因此拉伸试验中必须采用标准试件或比例试件,这样其有关性质才具可比性.
材料相同而长短不同的试件通常情况下延伸率是不同的(横截面面积与长度存在某种特殊比例关系除外).
2、 分析比较两种材料在拉伸时的力学性能及断口特征.
答:试件在拉伸时铸铁延伸率小表现为脆性,低碳钢延伸率大表现为塑性;低碳钢具有屈服现象,铸铁无.低碳钢断口为直径缩小的杯锥状,且有450的剪切唇,断口组织为暗灰色纤维状组织。铸铁断口为横断面,为闪光的结晶状组织。.
教师签字:_ _______
日 期:___ _____
二、压缩实验报告标准答案
实验目的:见教材。 实验原理: 见教材。
实验数据记录及处理: 例:(一)试验记录及计算结果
问题讨论:
1、分析铸铁试件压缩破坏的原因.
答:铸铁试件压缩破坏,其断口与轴线成45°~50°夹角,在断口位置剪应力已达到其抵抗的最大极限值,抗剪先于抗压达到极限,因而发生斜面剪切破坏。
篇二:材料力学实验报告答案
材料力学实验报告
评分标准 拉伸实验报告
一、实验目的(1分)
1. 测定低碳钢的强度指标(σs、σb)和塑性指标(δ、ψ)。 2. 测定铸铁的强度极限σb。
3. 观察拉伸实验过程中的各种现象,绘制拉伸曲线(P-ΔL曲线)。
4. 比较低碳钢与铸铁的力学特性。
二、实验设备(1分)
机器型号名称电子万能试验机
测量尺寸的量具名称游标卡尺 精度 0.02 mm
三、实验数据 (2分)
四、实验结果处理 (4分)
?s??b?
PsA0PbA0
=300MPa 左右 =420MPa 左右
=20~30%左右=60~75%左右
??
L1?L0
?100% L0A0?A1
?100% A0
?=
五、回答下列问题(2分,每题0.5分)
1、画出(两种材料)试件破坏后的简图。 略
2、画出拉伸曲线图。
3、试比较低碳钢和铸铁拉伸时的力学性质。
低碳钢在拉伸时有明显的弹性阶段、屈服阶段、强化阶段和局部变形阶段,而铸铁没有明显的这四个阶段。
4、材料和直径相同而长短不同的试件,其延伸率是否相同?为什