大型火力发电厂锅炉屏式过热器集箱安装焊缝热处理工艺改进措施The.PDF

大型火力发电厂锅炉屏式过热器集箱安装焊缝热处理工艺改进措施 林 华 (1．广西壮族自治区特种设备监督检验院 广西 南宁 530022） 摘要：本文针对中电广西防城港电力有限公司锅炉屏式过热器集箱焊缝热处理硬度不合格, 热处 理曲线不能满足标准要求进行原因分析，并采取了相应的改进措施，解决了屏式过热器集箱焊缝 现场热处理工艺技术难题，对屏式过热器集箱焊缝热处理工艺的编制具有参考作用。 关键词：屏式过热器集箱;焊接热处理;工艺措施 The improving measures of Boiler platen Superheater Header Weld’s Heat Treatment technology in the large power plant Lin hua (1.Guangxi Special Equipment Supervision and Inspection Institute GuangXi NanNing 530022) Abstract: This paper emphasizes on the analysis of the reasons for the Unqualified Heat Treatment Hardness and curves of Boiler platen Superheater Header Weld in the China Guangxi Fangchenggang Electric Power Co.Ltd, and the technological problems on the spot heat treatment technology were settled by taking the improving measures, The research will have a significant function for the heat treatment technology compilation of platen Superheater Header Weld. Key words: Platen Superheater headers ；welding heat treatment ；technological measure 中电广西防城港电力有限公司一期工程 无法绑扎，安装单位在进行热处理过程中由于 建设两台 60 万千瓦超临界燃煤发电机组，其 工艺不当，如热处理加热范围不够，布置的控 锅炉为东方锅炉(集团)股份有限公司生产的 温热电偶数量不足等原因，导致热处理工作未 超临界参数变压直流炉，型号为 DG1900/25.4- 能满足标准要求，如热处理升温速度太慢，恒 Ⅱ2 型，主要投资方为香港中华电力有限公司， 温时间不足，热处理曲线与工艺卡不吻合，焊 该公司项目质量管理很规范，安装单位必须严 缝硬度超标，屏式过热器出口集箱热处理工作 格按技术标准及施工方案进行施工及验收。由 被迫停止，中电广西防城港电力有限公司对此 于锅炉厂设计屏式过热器出口集箱时未充分 非常不满，要求安装单必须改进热处理工艺。 考虑现场实际施工条件和环境，集箱上的管座 本文通过对屏式过热器集箱焊口布置情况及 预留长度太短，致使现场安装焊缝焊前预热和 其热处理工艺不合理性进行原因分析，并提出 焊后热处理可操作性很差，加热片很难绑扎或 相应的热处理工艺改进措施，取得良好的效 1 果，保证热处理工作质量。