钢铁化学成分.doc

.. . 钢号 化学成分（%） 机械性能（≥） 　 　 C Si Mn P≤ S≤ Cr Ni Mo Cu V σb MPa σb MPa δ％ Ψ ％ HB AKv J 碳 钢 铸 件 ZG200-400 ≤0.20 ≤0.50 ≤0.80 0.04 0.04 ≤0.30 ≤0.30 ≤0.20 ≤0.30 ≤0.05 400 200 25 40 　 30 ZG230-450 ≤0.30 ≤0.50 ≤0.90 0.04 0.04 ≤0.30 ≤0.30 ≤0.20 ≤0.30 ≤0.05 450 230 22 23 　 25 ZG270-500 ≤0.40 ≤0.50 ≤0.90 0.04 0.04 ≤0.30 ≤0.30 ≤0.20 ≤0.30 ≤0.05 500 270 18 25 　　 22 ZG310-570 ≤0.50 ≤0.60 ≤0.90 0.04 0.04 ≤0.30 ≤0.30 ≤0.20 ≤0.30 ≤0.05 570 300 15 21 　 15 ZG340-640 ≤0.60 ≤0.60 ≤0.90 0.04 0.04 ≤0.30 ≤0.30 ≤0.20 ≤0.30 ≤0.05 640 340 10 18 　 10 WCA ≤0.25 ≤0.60 ≤0.70 0.04 0.045 ≤0.50 ≤0.50 ≤0.20 ≤0.30 ≤0.03 415～585 205 24 35 　 　 WCB ≤0.30 ≤0.60 ≤1.0 0.04 0.045 ≤0.50 ≤0.50 ≤0.20 ≤0.30 ≤0.03 485～655 250 22 35 　 　 WCC ≤0.25 ≤0.60 ≤1.20 0.04 0.045 ≤0.50 ≤0.50 ≤0.20 ≤0.30 ≤0.03 485～655 275 22 35 　 　 低 合 金 钢 ZG20CrMo 0.17～0.25 0.20～0.45 0.50～0.80 0.03 0.03 0.50～0.80 　　 0.40～0.60 　 　 460 245 18 30 　 24 ZG35CrMo 0.30～0.37 0.30～0.50 0.50～0.80 0.03 0.03 0.80～1.20 　 0.20～0.30 　 　 740～880 510 12 　 　 27 ZG40Cr 0.35～0.45 0.20～0.40 0.50～0.80 0.03 0.03 0.80～1.10 　 ≤0.15 　 　 630 345 18 26 ≥212 　 ZG15W1Mo1V 0.14～0.20 0.15～0.37 0.40～0.70 0.03 0.03 1.20～1.70 　 1.0～1.20 　 　 539 343 20 35 ≥140 　 WC1 ≤0.25 ≤0.60 0.50～0.80 0.04 0.045 ≤0.35 ≤0.50 0.45～0.65 ≤0.50 W≤0.10 450～620 240 24 35 　　 　 WC5 0.05～0.20 ≤0.60 0.40～0.70 0.04 0.045 0.50～0.90 0.60-1.0 0.90～1.20 ≤0.50 W≤0.10 485～655 275 20 35 　 　 WC6 0.05～0.20 ≤0.60 0.50～0.80 0.04 0.045 1.0～1.50 ≤0.50 0.45～0.65 ≤0.50 W≤0.10 485～655 275 20 35 　 　 WC9 0.05～0.18 ≤0.60 0.40～0.70 0.04 0.045 2.0～2.75 ≤0.50 0.90～1.20 ≤0.50 W≤0.10 485～655 275 20 35 　 　 4C ≤0.30 ≤0.80 ≤1.00 0.04 0.045 0.40～0.80 0.40～0.80 0.15～0.30 ≤0.50 ≤0.30 ≥620 ≥415 ≥18 ≥35 　 　 A487(MS-512-06) ≤0.30 ≤0.80 ≤1.00 0.04 0.04 0.40～0.80 0.40～0.80 0.15～0.25 ≤0.30 ≥655 ≥517 ≥18 ≥35 207-237　 　 低 温 钢 LCB(-46℃） ≤0.30 ≤0.60 ≤1.0 0.04 0.04 　 　 　 　 　 450～620 240 24 35 　 ≥18 LC3(-101℃） ≤0.15 ≤0.60 0.50～0.80 0.04 0.045 　 3.0～4.0 　 　 　 485～655 275 24 35 　 ≥20 CF8(-196℃） ≤0.08 ≤1.50 ≤1