酒钢CSP带钢卷取塔形控制实践.doc

酒钢CSP带钢卷取塔形控制实践 　　摘 要： 酒钢CSP卷取机卷取高强度厚规格和冷轧基料钢种时钢卷产生塔形和错层，严重影响产品质量和后续加工。针对这种情况，对各种塔形产生的原因进行了分析，对卷取过程中输出辊道、夹送辊、芯轴和助卷辊的速度控制、芯轴与轧机间的张力控制、侧导板控制，以及卷取区设备维护等方面进行了实践改进，通过实践总结出了常见塔形处理方法，目前卷取塔形问题有了很大改善。 　　关键词： 卷取机；侧导板；塔形；原因分析；控制改进 　　 　　Analysis and control telescope coils in CSP plant of JISCO 　　Zhang Ning 　　(JiuQuan Iron and Steel Group Co. Ltd.) 　　 　　Abstract The： telescope coils were produced when high strength thick gauge stripes and thin gauge stripes for cold mill were coiled in CSP plant of JISCO. In this situation, analyzing the causes of the telescope coils, speed controls and tension controls of run out tables , pinch rolls, mandrels, wrapper rolls , side guide and equipment improvements maintenance. Prevented different kinds of telescope are summarized. Adopting the effect measures, The telescope coils were almost eliminated. 　　Key words : coiler; side guide; telescope; analysis; improved; control 　　 　　1、前言 　　 酒泉钢铁（集团）有限责任公司的卷取机于2006年投入运行，卷取宽度设计范围为950～1680mm，带钢厚度设计范围0.8～12.7mm。在带钢生产时卷取过程中，参与过程控制的主要设备有侧导板、夹送辊、助卷辊和芯轴，当带钢头部经过层流冷却后，由侧导板引导，经夹送辊、斜槽板、助卷辊、直至被芯轴卷取。卷取机在卷取厚度大于8.0mm以上高强度钢种，例如：生产510L，590L等弯曲张力比较大的品种钢时，钢卷易产生塔形和错层，在生产薄规格冷轧料时也容易引起塔形。 　　 钢带卷取的塔形问题一直是影响酒钢CSP的产品质量的重要因素，从生产和销售情况来看，塔形钢卷会产生以下问题： 　　a.塔形钢卷不易吊装，易造成钢卷边部损伤； 　　b.塔形卷不易装运，会造成打包带断带，形成松卷； 　　c.供冷轧使用的塔形和错层会给后续加工造成困难和造成事故； 　　d.塔形和错层影响产品外观。 　　 因此酒钢对塔形问题十分重视，专门针对塔形问题??织技术人员攻关，制订修订技术标准和定期检验更换标准、实施技术改造方案，降低塔形率，提高产品合格率，获得了塔形卷的治理经验和可观的经济效益。 　　 　　2、钢卷塔形分类 　　 酒钢CSP生产线上有2台三助卷辊式地下卷取机，在带钢接近卷取机时，通过卷取机前的可调适侧导板将其对中导向，然后夹送辊引导带钢头部进入芯轴，芯轴与助卷辊配合完成带钢的卷取。卷取过程中出现的塔形现象主要分头部塔形、层间塔形和尾部塔形3类，另外也有部分是混合塔形。 　　 头部塔形。头部塔形式强制纠偏引起的塔形，起因是带头进入卷取机是已经偏离了中心线，被侧导强制性纠偏后，钢带重新回到中心线，头部就会出现塔形，这种塔形，如果在侧导板响应及时的情况下也能控制在正常范围之内，如果这时出现带头控制检测失误，就会出现塔形，同时也会引起头部松卷。 　　 层间塔形（错层）。主要是由于钢带的上下、左右抖动。引起抖动的原因是F6机架与夹送辊之间失张或张力波动大，侧导的磨损使位置控制不精确或不到位，压力控制超出了极限范围；夹送辊的辊缝偏差超限也会引起钢带产生侧向力，造成带钢向一侧跑偏，此时侧导板就要对带钢纠偏，由于高强度厚规格钢带的侧向推力比较大，侧导又因为带钢的侧向力推回，这样侧导和带钢之间反复推进推回，最后造成层间塔形。 　　 尾部塔形。尾部塔形的产生是轧制过程尾部钢带未在中心线上，在F6抛钢之后，钢带尾部失张，侧导板的纠偏作用消失，产生尾部塔形，夹送辊的辊缝偏差产生的侧向力也会加剧尾部塔形。