高支高密纯棉色织免烫衬衫面料的开发与生产.doc

高支高密纯棉色织免烫衬衫面料的开发与生产 　　摘要：高支高密纯棉色织面料经液氨整理后制成的抗皱免烫衬衫，手感轻柔滑爽，布面有真丝般的光泽，抗皱挺括，附加值高，是高档的衬衫面料。本文探讨了高支高密纯棉色织衬衫面料的设计开发及其生产，分析了生产技术难点，主要工序工艺参数及技术措施。 　　关键词：高支高密；纯棉；生产工艺；免烫；衬衫面料 　　中图分类号：TS106 文献标志码：A 　　The Development and Production of High-count High-density Pure Cotton Yarn-dyed Iron-free Shirting 　　Abstract： After liquid ammonia finish， high-count high-density pure cotton yarn-dyed fabric can be made into crease-resistant iron-free shirting with soft， smooth and crispy handle， silky shade on fabric surface and high value-added， which is an ideal fabric for making high-grade shirt. The paper discussed the design and production of high-count high-density pure cotton yarn-dyed shirting， and analyzed the key technical points， process parameters and technical measures in production. 　　Key words： high-count high-density； pure cotton； production process； iron-free； shirting 　　轻薄舒适是高档色织面料的发展趋势，近年来，纯棉衬衫面料开发采用更高的纱支与更大的密度，推动纯棉织物向高档化、多元化方向不断发展。我们开发了一系列高支高密纯棉织物，经液氨整理后制成抗皱免烫衬衫，手感轻柔舒适，布面具有真丝般的光泽，抗皱挺括，舒适性好，大大地提高了品质与档次，深受国内外消费者的青睐。 　　1 产品规格 　　纯棉高支高密色织衬衫面料系列规格如表 1 所示。 　　2 生产难点分析 　　高支高密织物一直是生产难度较大的品种，尤其是经纬纱线均在Ne 80以上时，在整经、浆纱、织造、修织等工序的生产难度更大。生产难点主要有：（1）高支高密织物由于纱号细、单纱强力较低，对原纱质量要求更高。（2）因单纱强力较低，在整经上百根纱万米断头率会明显升高，需要解决整经断头的问题。（3）因单纱强力较低，要求上浆时应有一个合适的上浆率，以增加纤维间的抱合力和纱线强力；经密大，织物总经根数多，浆纱覆盖系数增大，分绞、缠纱、倒并绞增多。因此，要选用性能先进的浆纱机，配置合理浆纱工艺参数。（4）因织物密度大、紧度高、总经根数多，织造过程中经纱摩擦和缠绕增加，纱线断头造成经向停台。高密度品种织造时毛羽粘连、开口不清，使布机断经增加，影响布面外观质量和生产效率；此外，高支色纱强力降低、吸浆快、张力控制难，在上浆过程中不能褪色，故浆料的选择、浆纱配方和上浆工艺参数应合理配置。 　　3 原纱指标 　　高支高密色织面料因经纬密度大、纱支细，浆纱与织造难度都较大，因此，为保证织物质量和织造效率，必须选用优质棉纱，如JC11.7 tex原棉配棉采用23.5%新疆长绒棉，JC9.7 tex原棉配棉采用40.9%新疆长绒棉，使其质量水平达到2001乌斯特公报25%左右水平。严格控制原纱质量，着重控制原纱的条干CV值、单纱断裂强度、单强CV值、粗节、细节、棉结等指标，尤其是条干CV值、单强CV值、细节水平至关重要。原纱质量指标见表 2。 　　4 主要工序工艺参数及技术措施 　　4.1 络筒 　　采用AC338型自动络筒机。络筒时纱线通道要清洁、光滑，断头自停装置良好。降低纱线在退绕过程中与设备之间的摩擦，防止毛羽增加。络筒工艺原则为低速度、轻张力、小伸长、保弹力，主要工艺参数如下：车速1 000 r/min，卷绕密度0.4 ～ 0.45 g/cm3。电清工艺：N（棉结）通道250%，S（短粗）通道截面增量150%、长度2.5 cm，L（长粗）截面增量40%，长度40 cm，T（长细）通道截面增量-30%、长度60 cm，张力器示数12。捻接器参数设定：解捻气压0.5 MPa，加捻气压0.5 MPa。