* * * 这是阳离子交换树脂的示意图 微球的粒径: 300 ~ 1200 μm (0.3 ~ 1.2 mm) 流通孔径: 1 ~ 100 nm (0.001 ~ 0.1 μm) 微球干重 40 ~ 60% T: -40 ~ + 40°C * * * * For the production of ultrapure water, we use synthetic activated carbon produced by the controlled pyrolysis of styrene beads. You can see from the microscope picture on the left side of the screen that this is a better defined media : the beads, for instance, are more regualr is size and shape. This is the activated carbon that we use in the Milli-Q systems packs. It is characterized by a faster binding kinetic of low molecular weight organics,and releases very little ions ,as well as very little organics. Therefore, synthetic activated carbon is suitable for Type I water production. * * 温度 温度对于RO的工作效率和产水速率都有很大的影响，包括高纯水的电阻率数值和温度也息息相关，所以Milli-Q Integral中有多处温度测定。 水压 自来水进水压力，RO膜前后的压力等等，水压的数值是反应机器各组件是否正常运行的重要参数。 电阻率 大家最耳熟能详的水质指标。Milli-Q Integral中有4个电阻率仪，从进水到RO水，到Elix水，直到超纯水都有对应的电阻率仪表表征各步的离子去除效果。 TOC TOC指标表征的是水中的有机物含量，这一指标目前越来越多的实验人员开始关注起来，当然，对于超纯水的TOC监测目前还只有少数几家厂家可以做到。 * 这是电导率的理论计算公式。 上面我们说过，水靠水中的离子导电。 这样，在单位电场作用下，单位时间内迁移的电荷数——也就是离子的浓度、单个离子电荷数（价位）和离子的迁移速度的乘积，在乘以法拉第常数（ 96480 库伦），将单位换算成Siemens/cm——也就是水的电导率了。 电阻率是电导率的倒数。 * 这个表格表现的是NaCl（ppb）浓度和电阻率/电导率变化的理论关系。我们看到，当NaCl的浓度仅为1ppb时，18.2Mohm.cm就迅速下降到。 其他的酸、碱、盐都与此类似。正因为电阻率值对微量的离子污染物异常敏感，因此我们用它来作为最有效的表征超纯水离子污染物的参数 NB : notice also that 1 ppb NaCl causes a drop of resistivity down to 17.6 Megohm.cm. The same effect can be obtained by an increase of the water temperature by 0.6°C (as shown in a previous slide) . * 由于水的离子积、离子迁移率均会随温度T变化，因此电阻率也是会随温度改变的。 如图所示，随着温度的提高，超纯水的导电能力得到加强，电阻率下降，而温度降低，电阻率则会上升。因此没有给定检测温度的电阻率值是不能表征水的纯度的。 为了方便不同实验之间用水纯度的比较，我们通常会同时测定水的电阻率和水温，然后将测得的电阻率换算成25°C的电阻率。当然，这种换算必须建立在准确测量温度的基础上，不然这种换算产生的偏差很大。 * The above experimentation carried over by A. Foley, demonstrates that an organic breakthrough can occur with little variation in resistivity.Water produced by a Milli-RO was stored in a reservoir and used to feed a Milli-Q. At t=0, sugar was dissolve